Microwave synthesis and electrochemical performance of a PtPb alloy catalyst for methanol and formic acid oxidation

► Microwave was used to rapidly synthesize PtPb alloy catalyst for methanol and formic acid oxidation. ► A core–shell structure with Pt core and shell of PtPb alloying. ► PtPb/C catalyst has much higher catalytic activity compared with commercial Pt/C and PtRu/C catalysts. ► Prominent advantages are...

Full description

Saved in:
Bibliographic Details
Published in:Electrochimica acta 2012-02, Vol.63, p.346-353
Main Authors: Huang, Yiyin, Zheng, Shiying, Lin, Xiujuan, Su, Liqing, Guo, Yonglang
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:► Microwave was used to rapidly synthesize PtPb alloy catalyst for methanol and formic acid oxidation. ► A core–shell structure with Pt core and shell of PtPb alloying. ► PtPb/C catalyst has much higher catalytic activity compared with commercial Pt/C and PtRu/C catalysts. ► Prominent advantages are excellent anti-poisoning ability and high stability. ► Peak current densities of methanol oxidation in 950th cycle on PtPb/C, PtRu/C and Pt/C are 870.6, 596.4 and 472.9mAmg−1Pt (or 4.53, 1.30 and 1.05mAcm−2), respectively. A PtPb alloy catalyst with a uniform core–shell structure was synthesized in a two-step rapid microwave-assisted polyol process. The X-ray diffraction (XRD) and transmission electron microscopy (TEM) data demonstrate that the core of this catalyst is a Pt particle, and the shell or completely alloyed nanoparticles are composed of a PtPb alloy with an hcp structure. The average diameter of the catalyst is approximately 5.9nm. The PtPb alloy catalyst exhibits enhanced catalytic activity and durability for methanol or formic acid oxidation. The anodic peak current densities for methanol oxidation at the 950th cycle on PtPb/C, PtRu/C (JM) and Pt/C (JM) catalysts are 870.6, 596.4 and 472.9mAmg−1 Pt, respectively. The formation of large numbers of oxides on the PtPb/C catalyst surface can enhance the anti-poisoning ability and catalytic durability of the catalyst.
ISSN:0013-4686
1873-3859
DOI:10.1016/j.electacta.2011.12.112