Toughness enhancement in architecturally modified Al6061-5 vol.% SiCp laminated composites

Damage tolerance improvement in discontinuously reinforced aluminum matrix composites has been examined through both extrinsic and intrinsic approaches by researchers. In this study, extrinsic mechanism was considered in the form of architectural modification in laminates comprising two exterior lay...

Full description

Saved in:
Bibliographic Details
Published in:International journal of damage mechanics 2015-03, Vol.24 (2), p.245-262
Main Authors: Monazzah, A Hosseini, Bagheri, R, Reihani, SM Seyed, Pouraliakbar, H
Format: Article
Language:English
Subjects:
Adhesive bonding
Aluminum matrix composites
Architecture
Energy consumption
Fracture toughness
Hot rolling
Laminates
Silicon carbide
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Damage tolerance improvement in discontinuously reinforced aluminum matrix composites has been examined through both extrinsic and intrinsic approaches by researchers. In this study, extrinsic mechanism was considered in the form of architectural modification in laminates comprising two exterior layers of Al6061-5 vol.% SiCp and an interlayer of Al1050. Hot roll bonding was utilized to fabricate laminates since interfacial adhesion of layers was controlled by means of rolling strain. The interfacial strength and fracture resistance of specimens were examined by shear and three-point bending test, respectively. Achievements demonstrated that the quasi-static toughness of laminates tested in crack divider orientation was greater than that of monolithic samples. Also, it was revealed that the initiation, propagation, and total toughness were influenced by interfacial adhesion. In the other words, interfacial bonding played a major role in energy absorption during fracture. Enhancement of the interfacial adhesion by an increment in rolling strain elevated the energy consumed for emergence and growth of debonded area.
ISSN:1056-7895
1530-7921
DOI:10.1177/1056789514529984