Magnetic properties of microwave-synthesized Mn-doped SnO sub(2) nanoparticles

Semiconductor nanostructures with dilute magnetic property are of great importance for different applications. However, this property depends on several factors including the synthesis route. In this work, manganese (Mn)-doped tin dioxide (SnO sub(2)) nanoparticles (NPs) at different concentrations...

Full description

Saved in:
Bibliographic Details
Published in:Applied physics. A, Materials science & processing Materials science & processing, 2016-11, Vol.122 (11), p.1-9
Main Authors: Salah, Numan, Habib, Sami, Azam, Ameer
Format: Article
Language:English
Subjects:
Doping
Magnetic properties
Manganese
Nanoparticles
Nanostructure
Semiconductors
Synthesis
Tin dioxide
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Semiconductor nanostructures with dilute magnetic property are of great importance for different applications. However, this property depends on several factors including the synthesis route. In this work, manganese (Mn)-doped tin dioxide (SnO sub(2)) nanoparticles (NPs) at different concentrations were synthesized by the microwave-assisted synthesis method and evaluated for their magnetic properties. The X-ray diffraction analyses revealed a single-phase rutile-type tetragonal structure, while SEM and TEM images showed fine NPs with average sizes around 10 nm. A considerable increase in value of the energy band gap by around 0.18 eV as a result of Mn doping was observed. This dopant has also increased the lattice d-spacing value, but slightly decreased the lattice constant c. The magnetic measurement result showed that all the microwave-synthesized Mn-doped SnO sub(2) NPs including the pure one have distinctly wide hysteresis loops, indicating that samples have room temperature ferromagnetism (RTFM). RTFM was further enhanced by Mn doping reaching maximum at a concentration of 0.3 mol%. This magnetism could be attributed to the presence of defects at the grain boundaries within the NPs, interfacing sites between the NPs, oxygen or tin vacancies and an optimum level of Mn dopant. The observed wide hysteresis loops in these samples might be due to the use of a surfactant at high concentration that could provide highly compact/tight NPs. These results might be useful for producing nanoscale magnets and magnetic memory devices.
ISSN:0947-8396
1432-0630
DOI:10.1007/s00339-016-0519-4