Using an added liquid to suppress drying defects in hard particle coatings
[Display omitted] •Capillary suspensions dry homogeneously without drying defects.•Connection between particle migration and trench or pinhole formation.•Capillary bridges between particles inhibit air invasion.•Capillary corner flow towards the coating surface maintains constant drying rate.•Capill...
Saved in:
Published in: | Journal of colloid and interface science 2021-01, Vol.582, p.1231-1242 |
---|---|
Main Authors: | , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | [Display omitted]
•Capillary suspensions dry homogeneously without drying defects.•Connection between particle migration and trench or pinhole formation.•Capillary bridges between particles inhibit air invasion.•Capillary corner flow towards the coating surface maintains constant drying rate.•Capillary flow towards the surface persists beyond full consolidation.
Lateral accumulation and film defects during drying of hard particle coatings is a common problem, typically solved using polymeric additives and surface active ingredients, which require further processing of the dried film. Capillary suspensions with their tunable physical properties, devoid of polymers, offer new pathways in producing uniform and defect free particulate coatings.
We investigated the effect of small amounts of secondary liquid on the coating’s drying behavior. Stress build-up and weight loss in a temperature and humidity controlled drying chamber were simultaneously measured. Changes in the coating’s reflectance and height profile over time were related with the weight loss and stress curve.
Capillary suspensions dry uniformly without defects. Lateral drying is inhibited by the high yield stress, causing the coating to shrink to an even height. The bridges between particles prevent air invasion and extend the constant drying period. The liquid in the lower layers is transported to the interface via corner flow within surface pores, leading to a partially dry layer near the substrate while the pores above are still saturated. Using capillary suspensions for hard particle coatings results in more uniform, defect free films with better printing characteristics, rendering high additive content obsolete. |
---|---|