Printable PICN Composite Mechanically Compatible with Human Teeth

• Published in: Journal of dental research 2021-12, Vol.100 (13), p.1475-1481
• Main Authors: Sodeyama, M.K., Ikeda, H., Nagamatsu, Y., Masaki, C., Hosokawa, R., Shimizu, H.
• Format: Article
• Language: English
• Subjects: Ceramics; Computer-Aided Design; Dental enamel; Dental restorative materials; Dentin; Enamel; Flexural Strength; Humans; Materials Testing; Mechanical properties; Nanoparticles; Physicochemical properties; Polymers; Rapid prototyping; Slurries; Surface Properties; Teeth
• ISSN: 0022-0345; 1544-0591
• DOI: 10.1177/00220345211012930

Polymer-infiltrated ceramic network (PICN) composites are mechanically compatible with human enamel, and are therefore promising dental restorative materials. Fabrication technology for PICN composites used in tooth restorative material has been established through computer-aided design/computer-aided manufacturing (CAD/CAM) milling, however, to date, has not been successfully developed using 3-dimensional (3D) printing. This study aimed to develop a 3D-printable PICN composite as a restorative material. The PICN composite was fabricated using a specific method based on 3D printing. A 3D-printable precursor slurry containing a high concentration of silica nanoparticles was produced and 3D-printed using stereolithography (SLA). The 3D-printed object was sintered to obtain a nano-porous object, and subsequently infiltrated and polymerized with resin monomer. Three different fabrication condition combinations were used to produce the 3D-printed PICN composites, which were characterized based on microstructure, mechanical properties, inorganic content, physicochemical properties, and overall shrinkage. The 3D-printed PICN composites were also compared to 2 commercially available CAD/CAM composite blocks, namely a PICN composite and a dispersed-filler composite. The 3D-printed PICN composites exhibited a nano-sized dual-network structure comprising a silica skeleton with infiltrated resin. The 3D-printed PICN composite exhibited a similar Vickers hardness to enamel, and a similar elastic modulus to dentin. The 3D-printed PICN composite exhibited comparable flexural strength (>100 MPa) to the CAD/CAM block, and acceptable water sorption and solubility for practical use. Further, the 3D-printed model-crown underwent isotropic shrinkage during sintering without fatal deformation. Overall, the potential of this 3D-printable PICN composite as a restorative material with similar mechanical properties to human teeth was successfully demonstrated.