An experimental investigation of gas-phase combustion synthesis of SiO2 nanoparticles using a multi-element diffusion flame burner

This work presents the results of an experimental investigation of gas-phase combustion synthesis of silica (SiO2) particles using a multi-element diffusion flame burner (MEDB, a Hencken burner). Silane (SiH4) was added to hydrogen/oxygen/argon (H2/O2/Ar) flames to produce SiO2 nanoparticles at vari...

Full description

Saved in:
Bibliographic Details
Published in:Combustion and flame 2002-10, Vol.131 (1-2), p.98-109
Main Authors: WOOLDRIDGE, M. S, TOREK, P. V, DONOVAN, M. T, HALL, D. L, MILLER, T. A, PALMER, T. R, SCHROCK, C. R
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:This work presents the results of an experimental investigation of gas-phase combustion synthesis of silica (SiO2) particles using a multi-element diffusion flame burner (MEDB, a Hencken burner). Silane (SiH4) was added to hydrogen/oxygen/argon (H2/O2/Ar) flames to produce SiO2 nanoparticles at various burner operating conditions (phi = 0.47-2.16). To characterize the burner performance, temperature measurements were made using water absorption spectroscopy and uncoated, fine-wire thermocouples. The results demonstrated the non-premixed flow arrangement of the fuel tubes and oxidizer channels of the MEDB provided uniform, approximately ID conditions above the surface of the burner, with temperature variations of less than +/-3 percent in the transverse direction (parallel to the surface of the burner) for elevations above the mixing region (z = 0-7 mm), extending to heights not less than 30 mm. At heights above the mixing region, approximately constant axial temperatures were also observed. Silica particle formation and growth were examined for comparison with current understanding of the physical mechanisms important in combustion synthesis of SiO2. The particle properties were determined using TEM imaging. The current study demonstrates the utility of the MEDB in providing a controlled environment for fundamental studies of gas-phase combustion synthesis phenomena, as well as offering broad flexibility in experimental design with control over process variables such as temperature field, particle residence time, scalable reactant loading, and particle precursor selection. (Author)
ISSN:0010-2180
1556-2921
DOI:10.1016/S0010-2180(02)00403-0