Prediction of Ductile Fracture in Cold Forging of Aluminum Alloy

In this paper, the limitation and applicability of the ductile fracture criteria based on a work hypothesis and Cockcroft and Latham were investigated. For this purpose, experimental and numerical investigations for simple upsetting were conducted for aluminum alloys Al1100-O, Al2024-T3, Al6061-T4,...

Full description

Saved in:
Bibliographic Details
Published in:Journal of manufacturing science and engineering 1999-08, Vol.121 (3), p.336-344
Main Authors: Kim, Hong-Seok, Im, Yong-Taek, Geiger, Manfred
Format: Article
Language:English
Subjects:
Aluminum alloys
Applied sciences
Cold working
Crack initiation
Ductility
Exact sciences and technology
Failure (mechanical)
Finite element method
Forging and extrusion
Forming
Metals. Metallurgy
Numerical analysis
Production techniques
Tensile stress
Upsetting (forming)
Viscoplasticity
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:In this paper, the limitation and applicability of the ductile fracture criteria based on a work hypothesis and Cockcroft and Latham were investigated. For this purpose, experimental and numerical investigations for simple upsetting were conducted for aluminum alloys Al1100-O, Al2024-T3, Al6061-T4, and Al7075-T4. As a result, the fracture mode of each alloy was observed. The study was extended for pin-shape cold forging of Al1100-O and Al6061-T4 to compare the likeliness of fracturing according to two criteria. Based on experimental data of simple upsetting, the damage factors for the same two criteria were calculated by adopting rigid-viscoplastic finite element analysis. With this approach, the prediction of surface cracking was attempted by comparing the calculated limiting damage factors between simple upsetting and pin-shape forging. It was observed in simple upsetting that Cockcroft and Latham’s criterion gave a more reasonable prediction for crack initiation site than work hypothesis, but the limiting damage factors differ depending on the process. In spite of the differences, however, Cockcroft and Latham’s criterion might be useful in designing upsetting-like cold forging processes in which the influence of the induced circumferential tensile stress on failure is dominant.
ISSN:1087-1357
1528-8935
DOI:10.1115/1.2832686