Optical analysis of the microstructure of a Mo back contact for Cu(In,Ga)Se sub(2) solar cells and its effects on Mo film properties and Na diffusivity

The microstructures of molybdenum (Mo) thin films deposited at pressures from 3.3 to 10.3 mTorr were characterized, and the relationships between these microstructures and the properties of the films (residual stress and electrical resistivity) were investigated. In the low deposition pressure regim...

Full description

Saved in:
Bibliographic Details
Published in:Solar energy materials and solar cells 2011-11, Vol.95 (11), p.2959-2964
Main Authors: Yoon, Ju-Heon, Cho, Sunghun, Kim, Won Mok, Park, Jong-Keuk, Baik, Young-Joon, Lee, Taek Sung, Seong, Tae-Yeon, Jeong, Jeung-Hyun
Format: Article
Language:English
Subjects:
BOUNDARIES
Contact
COPPER INDIUM SELENIDE
DEPOSITION
DIFFUSION
ELECTRICAL CONDUCTIVITY
Electrical resistivity
Grain boundaries
Microstructure
MICROSTRUCTURES
Porosity
RESIDUAL STRESS
Solar cells
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The microstructures of molybdenum (Mo) thin films deposited at pressures from 3.3 to 10.3 mTorr were characterized, and the relationships between these microstructures and the properties of the films (residual stress and electrical resistivity) were investigated. In the low deposition pressure regime (region I, below 7 m Torr), the residual stress in the tensile direction increases with increasing pressure and the electrical resistivity increases gradually, but at high deposition pressures (region, above 7 m Torr) the residual stress is reduced and the resistivity increases more steeply. These variations of the properties of the Mo films in the low pressure regime are due to the variation in grain size; the carrier mobility decreases due to increased grain boundary (GB) scattering and the tensile stress increases due to increased atomic attraction across the GBs. In contrast, the porosity of the Mo films increases significantly in the high pressure regime, as demonstrated with variable angle spectroscopic ellipsometry (VASE). Most of these pores are believed to be present along the grain boundaries of the Mo films, so their presence reduces the GB attraction and thus the tensile stress and enhances the carrier scattering. The high porosity of the Mo back contact was shown with secondary ion mass spectroscopy profiling to accelerate the Na diffusion from soda-lime glass into the Cu(In,Ga)Se sub(2) (CIGS) film.
ISSN:0927-0248
DOI:10.1016/j.solmat.2011.02.030